Featured products
Competitive price
- Dibenzylamine 2020/05/23
Dibenzylamine(DBA) Chemical NameN,N-DIBENZYLAMINE;N-(Phenylmethyl)-benzenemethanamine,Dibenzylamine Molecular Formula...
- Benzylamine 2020/01/12
Benzylamine Chemical Name N-BENZYLAMINE Molecular Formula C7H9N Molecular Weight 107.15 CAS No.: 100-46-9 Specifi...
- Rubber accelerator MTT 2018/03/10
Konson® Rubber Accelerator MTTChemical Name :3-Methylthiazolidine-2-Thione Molecular Formula C4H7NS2...
- Hydroquinone 2016/04/09
Hydroquinone (HQ) Chemical Name 1,4-Benzenediol Molecular Formula C6H6O2...
rubber accelerator TBSI
Pubdate:2012/02/21 INDUSTRIES PRODUCTS AND SERVICES RUBBER Rubber Chemical views:580
Rubber Accelerator TBSI
Chemical Name: N,N-bis(1,3-benzothiazol-2-ylsulfanyl)-2-methylpropan-2-amine
Molecular Formula C18H17N3S4
Molecular Weight 403.61
CAS No. 3741-80-8
Specifications Q/KS167-2012
Items | Specifications |
Appearance | Light-white powder |
Initial Melting Point, ℃ Min | 128 |
Heat Loss, % Max | 0.50 |
Ash, % Max | 0.50 |
Residue on 150μm Sieve1, %max | 0.1 |
Description TBSI can replace NOBS which is carcinogenic and does not generates the nitrosamines as
primary amine-based accelerator . The rubber added with TBSI can obtain good
scorch safety and lower vulcanization rate, and show good curing reversion resistance,
high modulus and lower heat generation, which optimizes adhesion between rubber and
brass coated steel cord. Its physical properties and dynamic properties of cured rubber
are similar with NOBS and DCBS cured rubber. It can also replace the blend of primary
amine accelerator TBBS or CBS and scorch retarder CTP and be used alone, which makes
it ideal for thick articles requiring a balanced cure and provides improved reversion
resistance both during extended cure times at elevated temperatures and during product
service life.
Dosage: NR: 0.5 – 1.5 phr IR: 0.5 – 1.5 phr SBR: 0.5 – 1.5 phr
NBR: 0.5 – 1.5 phr HNBR: 0.5 – 1.5 phr
Applications : This product will not generate the carcinogenic substance- nitrosamines which be
known more secure from NOBS, DIBS and DCBS under the same operation temperature.
It can be used in NR, SBR, Butadiene rubber and IR. Especially apply to the furnace
black sizing material with strong acid, showing the much better activity than CBS and
NOBS.
Storage : The product should be stored in the dry and cooling place with good ventilation,avoiding
exposure of the packaged product to direct sunlight.
Packing : In 25kg paper bags with plastic inner.